Using SQUID VSM Superconducting Magnets at Low Fields
Contents
1. May 2010 moment arb units 40 20 0 20 40 real or reported magnetic field Figure 1 A magnetically reversible material blue curve can appear hysteretic red curve due to superconducting magnet remanence Note the inverted clockwise nature of the loop field error gauss applied magnetic field tesla Figure 2 Field error defined in text vs the charge field in a typical SVSM superconducting magnet Note the negative sign of the field error when decreasing from positive fields Note also that the error is generally not symmetric between and up and down legs and is peculiar to each magnet Another important feature to notice in Fig 2 is that the field error is negative when discharging from positive fields That is if setting zero field in linear charging mode from 1 tesla or above the resulting field at the sample will be about 20 gauss in this example So if one wants to reach true zero field it means stopping the field discharge short at 20 Oe instead of overshooting zero field as one might intuitively think see footnote 3 for a discussion of magnetism units Finally note the asymmetry between the values of field error for up and down ramping directions It has Quantum Design Application Note 1500 011 Rev AO 3 May 2010 been observed that the field error magnitude near zero field can differ by up to 15 gauss this is a property of a particular magnet for the different charging directions Figure 3 shows the2. setting the field to zero from an initial field above 1 tesla in oscillate mode This will also attentuate the flux creep effects Remanence can be further reduced down to lt 0 05 gauss by using the Ultra Low Field option for the SQUID VSM which employs a fluxgate magnetometer and the modulation coil in the magnet to compensate trapped flux from the magnet Once a low remanence state has been achieved in the magnet you can make measurements at low fields 100 Oe lt H lt 100 Oe without inducing a significant amount of remanence However a field of 1 kOe will already introduce a lot of pinned flux in the magnet Some measurement situations most commonly M H loops from high fields through zero field do not permit the use of low field techniques discussed above In this case there are some guidelines we recommend in order to achieve best results e Determine the magnet remanence and flux creep properties of your magnet see Figs 2 5 by using a pure paramagnetic sample such as the Er Y AG standard sample 4500 636 or a Dy20 pellet 4041 008 that is free of any measureable amount of ferromagnetic impurities very important a ferromagnetic signature will lead to an underestimate of the real magnet remanence value this option is good since in principle the M H slope for these materials is very nearly constant at 300 K so one can determine the absolute field error at each field contact apps qdusa com for more information e
3. O uantum Design j Application Note 1500 011 Using SQUID VSM Superconducting Magnets at Low Fields Abstract The superconducting magnet used in SQUID VSM is capable of generating fields up to 7 tesla 7x10 gauss with the value determined to a very high degree of accuracy over most of this range The magnetic field value reported to the user is based only on the current flowing from the magnet power supply At low fields less than 1 tesla the magnetic field experienced by the user s sample can deviate significantly from the reported magnetic field The magnitude of this field error as much as 40 gauss in SQUID VSM magnets The origin of this effect is described and methods for its mitigation are outlined A similar application note 1070 207 discusses these effects in the context of PPMS magnets Section I Introduction When using a superconducting solenoid to control the magnetic field in an experiment the user must be aware of pinned magnetic flux lines and flux movement within the magnet in order to better know the magnetic field at the location of the user s experiment This application note will discuss how these effects manifest in the magnet used for the Quantum Design SQUID VSM As the title implies the effects are of greatest relative significance at low fields and are very important to keep in mind when conducting research on soft magnetic materials whose magnetic state is strongly affected by small changes in mag
4. The remanence properties of the magnet are very reproducible as long as the same field charging recipe is followed each time thus once the field error table is determined by using a standard sample you can run the same field charging sequence on your sample and apply this field correction alternately you can modify the field set points of the measurement protocol so that the actual field is the desired one in the example from Fig 2 setting 20 Oe from positive high fields will produce a field at the sample of 0 Oe In conclusion one must be cautious when using a magnet used for generating 10 gauss to also accurately generate fields on the order of 10 gauss By understanding the basic operating principles of a superconducting magnet and by following the guidelines laid out above it is possible to greatly reduce artifacts in the reported magnetic field While we have focused here on the instance of the Quantum Design SQUID VSM the effects of remanence flux creep and persistent switch leakage currents discussed in this application note are relevant to any superconducting magnet with a superconducting switch Quantum Design Application Note 1500 011 Rev AO T7 May 2010 l M Tinkham Introduction to Superconductivity McGraw Hill 1996 Soft magnetic materials characterized using a superconducting solenoid as magnetic source Giovanni Mastrogiacomo Jorg F L ffler and Neil R Dilley Appl Phys Lett 92 082501 2008 DOI
5. linear mode and stabilized The effects shown here are seen to be independent of the initial field providing it was larger than 1 tesla These unusual observations can be explained by the fact that a small amount of pinned remanent magnetic flux in the magnet escapes from the magnet windings into the bore of the magnet In order to understand this note that when the QuickSwitch is in the superconducting state it will sustain small DC currents without dissipation This means that the current in the magnet can differ slightly from the current at the power supply when the QuickSwitch is in the superconducting state a fact which should be kept in mind for the discussion below As illustrated in the table and the accompanying figure below a magnet is originally in its virgin state 1 in which no flux is pinned inside it Upon heating opening the QuickSwitch and passing current in the magnet windings 2 a positive field is generated in the sample space at the center After removing the current in the magnet and cooling closing the QuickSwitch 3 some flux remains pinned in the magnet and has the same sign as the original field because it resulted from field lines penetrating the magnet at positive fields However the stray fields from these dipoles are of course of the opposite sign hence the negative initial remanent field at the sample location after discharging from positive fields After an hour in this state a small fraction of the pi
6. typical magnitude of the field error in a 7 tesla SQUID VSM magnet Note the log normal plot style necessitated by the large variation in the field error as a function of applied field As with the other figures this should not be used to generate a correction for data taken on a different system as the magnitude of the remanence varies from magnet to magnet Rather these figures should be used for their qualitative information absolute field error gauss applied magnetic field tesla Figure 3 Typical magnitude of average field error averaged between up and down ramp directions as a function of the magnet field for a SQUID VSM magnet Note that the field error can be as much as 15 gauss different between up and down ramp directions 4 Application Note 1500 011 Rev AO Quantum Design May 2010 set zero field linearly from 7 tesla l set zero field again field at sample gauss 0 20 40 BO 80 100 120 time min Figure 4 The magnetic field at the sample location as measured using a paramagnetic Dy203 sample slowly drifts by about 1 gauss upon setting zero field in LINEAR mode from 7 tesla After 1 hour the field was once again set to zero which heats the QuickSwitch and removes persistent currents See the diagram on the next page for an explanation of this phenomenon The effect of magnetic flux motion on the magnetic field at the sample location is illustrated in Fig 4 The field was set from 7 tesla to zero in
7. 10 1063 1 2838733 gt Note on the magnetic units convention we refer here to the magnetic field B in units of gauss where 10 gauss tesla and it represents the real magnetic field at the sample In contrast the magnetic induction H is expressed in oersted Oe and being defined as the field due to free currents this is the one that the user controls when setting a current at the magnet power supply In SI units B Uo H M where M is the magnetization density and is defined as arising from bound currents For more information see the Magnetic Units Conversion Table under Technical Resources at the Quantum Design website www qdusa com For viewing clarity in the figure the magnetic field lines in the superconductor do not show the supercurrent vortices that generate the magnetic field gt Consider the persistent magnet as a superconducting ring of inner dimension of R and the pinned flux line in the superconductor with a radius r where R gt gt r Referring to the states in Table 1 we must compare the magnetic field at the sample location taken as the origin between the initial remanent state 3 and when the vortex moves out of the ring into the middle 4 We know that flux is conserved B R r B 0 R That is the flux enclosed on vortex at position R at the inner bore of the magnet is compared with field in the bore of the magnet after the vortex moves out The equation above approximates the magnet
8. ed for our case when the magnet current is set back to zero from a high field some of these pinned flux lines remain behind and create a small magnetic field seen at the sample location 2 Flux creep and escape over time some of these pinned magnetic flux lines will redistribute and may even leave the wire material altogether The term flux creep describes the diffusion of flux lines inside a superconductor At a stable magnetic field escape of flux from the interior of the wire can lead to induced currents in the magnet due to the topology of the superconducting magnet An outline of this note is as follows Section II will discuss the first two effects of remanence and flux motion Section III presents methods for mitigating the magnetic field artifacts that have been described Before reading this application note it is important to understand the basics of magnetic field control in the SQUID VSM especially the principle of the superconducting QuickSwitch as described in section 3 4 of the SQUID VSM User Manual Familiarity with superconducting phenomena especially the mixed state of type II superconductors is also highly recommended as this note will not provide that background see ref 1 Section II magnet remanence and flux motion The effect of magnet remanence at low fields is an offset error in the reported magnetic field This offset is dependent on the magnet history and is opposite in sign when coming from positive
9. ic field B as constant over the area of the loops in both cases While this is not strictly true the error is small compared with the amplification effect we are observing and hence is neglected 2 magnetic moment of vortex M mr I where is the current flowing around perimeter Ji magnetic field at center of the vortex a current ring B R mea 2r 4 3 put this value of Z into above expression for moment m B R r Ho m magnetic field at sample location due to pinned flux dipole B 0 e tT r 3 BAR r insert expression for m from above B 0 ae z Use flux conservation equation to compute ratio of field seen at sample in state 4 vs state 3 B 4 0 R B 0 r Since R 2 5cm and r 10 cm this amplification is over x1000 This is why a tiny amount of flux creep out of magnet will have a large effect on the field seen at the sample location 8 Application Note 1500 011 Rev AO Quantum Design May 2010
10. netic fields near zero Quantum Design does not incorporate a field sensor such as a Hall sensor in its instruments The magnetic field reported by the SQUID VSM 1s based on the current that is being generated in the magnet power supply if the magnet is charging or the last current that was sourced from the power supply when it was connected to the magnet if the QuickSwitch on the magnet has been closed The magnet power supply current is translated into a magnetic field using a constant field to current conversion factor or B I ratio for that given magnet This yields a magnetic field value that is very accurate at higher fields above about tesla There are two phenomena that cause the SQUID VSM reported magnetic field to differ from the actual magnetic field at the location of the user s sample Below is a brief summary of these effects The remainder of this application note will describe each these phenomena in greater detail 1 Magnet remanence alloys such as those used in the windings of superconducting magnets will permit the magnet field to enter the superconducting material as threads of quantized magnetic flux when placed in sufficiently large magnetic fields These flux lines are pinned and immobilized at defects in the material Movement of flux lines Quantum Design Application Note 1500 011 Rev AO May 2010 causes energy dissipation and can destroy the superconducting state When the magnetic field is remov
11. nned flux lines have escaped from the magnet windings and are in the bore of the magnet 4 Since this flux is now in free space it must be represented by currents flowing in the magnet and these are in the direction of the original magnetic field Since the magnet is superconducting the QuickSwitch acts as a persistent switch at small currents like this these currents will not dissipate The small amount of flux escape has a large effect on the field at the sample location due to a field amplification effect the field seen at the sample location when the flux has moved into the bore of the magnet is much larger than the stray field when that same amount of flux was pinned in the magnet Upon heating the QuickSwitch and setting zero field 5 the power supply removes the positive current in the magnet and the field that remains at the sample location is due to the stray fields from the remaining pinned vortices in the magnet The magnetic field at the sample is nearly the same as in state 3 because the vast majority of the flux has remained pinned in the magnet Quantum Design Application Note 1500 011 Rev AO 5 May 2010 t iew of magnet magnet state remanent remanent 1 hour remanent reconnected 1 6 Application Note 1500 011 Rev AO Quantum Design May 2010 Section III mitigating magnetic field artifacts in measurements The magnitude of the remanence in the magnet can typically be reduced down to 1 2 gauss by
12. versus negative fields Figure 1 below illustrates how this offset manifests in DC magnetometer data for a sample that is magnetically reversible If one plots the magnetic moment vs the reported SQUID VSM magnetic field the red curve results Note that the hysteresis curve is inverted so that there is an apparently negative coercivity for the sample On the other hand if one were to plot the moment vs the actual magnetic field at the sample location the reversible blue M H curve results While it is unphysical for the entire M H hysteresis loop to be inverted it implies continuous heat absorption by the material as one cycles the field it is possible to have a locally inverted region of the loop The existence of locally inverted hysteresis loops is of interest to the research community so it is important to discern real sample physics from instrument artifacts as pointed out in ref 2 If we define the field error as field error real magnetic field at the sample reported field and plot this quantity as a function of the field in a typical SQUID VSM magnet see Fig 2 we see that the absolute error decreases at higher fields the sign of the field error depends on the direction of magnet charging and that switching the field charging direction results in the field error traversing to the appropriate leg in a short field duration see traversing lines at 3 and 5 tesla 2 Application Note 1500 011 Rev AO Quantum Design